Photoactive mixture of acrylic monomers and chromophore-substituted halomethyl-1-triazine

ABSTRACT

Photopolymerizable mixture of (a) acrylic monomer such as 95 parts of an alkyl acrylate and 5 parts of acrylic acid and (b) 0.01 to 2 parts by weight of a chromophore-substituted-halomethyl-s-triazine such as ##STR1## The novel mixtures are primarily useful as pressure-sensitive adhesive mixtures.

CROSS-REFERENCE

This application is a division of applicant's copending application Ser. No. 121,404, filed Feb. 14, 1980 now U.S. Pat. No. 4,330,590.

BACKGROUND TO THE INVENTION

Pressure-sensitive adhesive tape is generally manufactured by coating onto a backing sheet a solution or emulsion of a pressure-sensitive adhesive polymer and heating the coating to drive off the volatile vehicle. Belgian Pat. No. 675,420 which was published May 16, 1966, concerns a process for making pressure-sensitive adhesive tape which evolves essentially no volatiles. While maintaining an inert atmosphere, a mixture of acrylic monomers and a photoinitiator is coated onto a backing sheet and then polymerized with ultraviolet radiation to a pressure-sensitive adhesive state.

U.S. Pat. No. 4,181,752 (Martens at al.) discloses a process for making pressure-sensitive adhesive tape which, like that of Belgian Pat. No. 675,420, involves the photopolymerization of acrylic monomers. While the Belgian patent discloses nothing of the specific intensity and the specific spectral distribution of the irradiation, the Martens Patent discloses that these must be controlled in order to attain desirably high cohesive strength and also to attain high peel resistance. It teaches that the polymerizable mixture should be subjected to radiation in the near ultraviolet region at a rate of irradiation in the 300-400 nanometer wavelength range of not more than 7 milliwatts per square centimeter of the mass exposed. Any radiation shorter than 300 nanometers is limited to not more than about 10% of the energy in the 300-400 nanometers. Because the same specific intensity and specific spectral distribution of the irradiation are preferred for the practice of the present invention, the disclosure of the Martens patent is here incorporated by reference.

Martens teaches that the pressure-sensitive adhesive layer may be crosslinked, particularly where it is desired to increase the cohesive strength of the adhesive without unduly affecting its compliance. This can be achieved by utilizing a photoactive crosslinking agent in conjunction with the photoinitiator. Preferred as the photoactive crosslinking agent are certain chromophore-substituted vinylhalomethyl-s-triazines such as 2,4-bis(trichloromethyl)-6-p-methoxystyryl-s-triazine which has the formula ##STR2## This compound is hereinafter called "MOST".

German Offenlegungsschrift No. 27 18 259 (Buhr) which was laid open Nov. 11, 1978, says that MOST and similar styryl-s-triazines are relatively complicated to prepare. It suggests that equally useful compounds can be prepared more easily, among which are ##STR3## wherein each of R₁ and R₂ may be, among other things, H or alkoxy, one of R₁ and R₂ may be Cl or Br, and m and n are integers from 0 to 3 and m+n does not exceed 5. U.S. Pat. No. 4,184,323 is essentially identical to the Offenlegungsschrift.

OTHER PRIOR ART

U.S. Pat. No. 3,779,778 (Smith et al.) teaches that MOST and similar styryl-s-triazines (having at least one trihalomethyl group and at least one chromophoric moiety conjugated with the triazine ring by ethylenic unsaturation) are useful as photolyzable acid progenitors for producing positive acting lithographic plates and the like. U.S. Pat. No. 3,987,037 (Bonham et al.) claims MOST and similar styryl-s-triazines and illustrates uses comparable to those shown in U.S. Pat. No. 3,779,778.

THE PRESENT INVENTION

As does the aforementioned Martens patent, the present invention primarily concerns a photocrosslinkable mixture of acrylic monomers such as alkyl acrylates, especially those which photopolymerize to a pressure-sensitive adhesive state and become crosslinked during the photopolymerization. As in Martens the photocrosslinkable mixture includes a photoactive agent which is a chromophore-substituted halomethyl-s-triazine, but this differs from MOST in that it has no styryl group. The photoactive s-triazine employed in the present invention can be made by a more simple and hence more economical process than can MOST, has better solubility in acrylic monomer mixtures than does MOST, and tends to provide desirably shortened reaction times and somewhat greater tolerance to oxygen. MOST tends to lend a yellowish color whereas the photoactive s-triazine employed in the invention usually produces no observable color, or in any case much less color than does MOST.

While the present invention primarily concerns (1) photopolymerizable mixtures of acrylic monomers which polymerize and become crosslinked when subjected to ultraviolet radiation, it also concerns (2) photoactive mixtures of acrylic polymers which become crosslinked when subjected to ultraviolet radiation and (3) photoactive mixtures of acrylic monomers which polymerize when exposed to ultraviolet radiation without becoming crosslinked.

Specifically, the present invention concerns a photoactive mixture comprising by weight

(a) 100 parts of a composition or a polymer of 50-100 parts of substituted or unsubstituted mono- or multi-functional alkyl acrylate or methacrylate monomers (all of which are hereinafter collectively referred to as "acrylic monomer") and 0-50 parts of copolymerizable monoethylenically unsaturated monomer; and

(b) 0.01 to 2 parts of a chromophore-substituted halomethyl-s-triazine of the formula ##STR4## wherein R₁, R₂, R₃, and R₄ are independently hydrogen, or alkoxy (preferably methoxy or ethoxy) groups, and 1 to 3 of R₁, R₂, R₃, and R₄ are hydrogen.

Preferably the alkoxy groups have not more than 12 carbon atoms (see U.S. Pat. No. 3,954,475). Preferably both R₂ and R₃ are alkoxy, because this tends to provide shorter reaction times. Adjacent alkoxy substituents may be interconnected to form a ring, specifically ##STR5## wherein n is 1, 2 or 3. This improves solubility in acrylic monomer.

The photoactive s-triazine component (b) may be prepared by the co-trimerization of an aryl nitrile with trichloroacetonitrile in the presence of HCl gas and a Lewis acid such as AlCl₃, AlBr₃, etc. [Bull. Chem. Soc. Japan, Vol. 42, page 2924 (1969)].

When photopolymerizing acrylic monomer, it may be desirable to do so stepwise. The preferred first step is to mix acrylic monomer with a photoinitiator which is not a crosslinking agent such that the dissolved amount of the photoinitiator provides up to 0.5% by weight of the mixture.

The second step is to expose the mixture to ultraviolet radiation to provide a partially-polymerized syrup having a viscosity of 300 to 20,000 centipoise at ordinary room temperature. Unless acrylic monomer were first at least partially polymerized, the viscosity of the mixture would be too low to provide uniform coatings of thicknesses most useful for pressure-sensitive adhesive tapes, e.g., 25 to 250 micrometers. The partial photopolymerizing may be stopped at any point simply by turning off the ultraviolet radiation.

The third step is to mix with said syrup the above-identified photoactive s-triazine component (b). The modified syrup may be coated onto a backing member and exposed to ultraviolet radiation to complete the polymerization. Alternatively, the third step may be performed using a syrup which has been prepared by conventional thermal polymerization techniques and has been quenched with air to attain the desired viscosity.

When an uncrosslinked polymer of acrylic monomer is mixed with the photoactive s-triazine component (b) and the mixture is exposed to ultraviolet radiation, the polymer becomes crosslinked if the acrylic monomer comprises an alkyl acrylate. For example, a pressure-sensitive adhesive polymer of an alkyl acrylate which has been polymerized in emulsion or solution may be dissolved in an organic solvent and then mixed with the photoactive s-triazine. After coating this solution onto a flexible backing member and evaporating the solvent, exposure of the coating to ultraviolet radiation causes crosslinking of the polymer. By using an opaque backing member to shield the dried coating from accidental ultraviolet radiation, the uncrosslinked tape may be marketed in commerce and eventually crosslinked by ultimate consumers.

Photoinitiators which are useful for partially polymerizing acrylic monomer without crosslinking include the benzoin ethers (such as benzoin methyl ether or benzoin isopropyl ether), substituted benzoin ethers (such as anisoin methyl ether), substituted acetophenones (such as 2,2-diethoxyacetophenone and 2,2-dimethoxy-2-phenylacetophenone), substituted alpha-ketols (such as 2-methyl-2-hydroxypropiophenone), aromatic sulfonyl chlorides (such as 2-naphthalene-sulfonyl chloride) and photoactive oximes [such as 1-phenyl-1,1-propanedione-2-(O-ethoxycarbonyl)oxime]. They may be used in amounts which as dissolved provide about 0.001 to 0.5 percent by weight of the alkyl acrylate or methacrylate monomer, preferably at least 0.01 percent.

After adding the above-identified photoactive s-triazine component (b) to acrylic monomer, whether or not partially polymerized to provide a coatable syrup, the polymerization quickly goes to completion when subjected to ultraviolet radiation. If the acrylic monomer comprises alkyl acrylate, the polymer simultaneously becomes crosslinked. Although the polymerization is exothermic, coatings as thick as 0.5 mm have been quickly polymerized uniformly. To form uniform, bubble-free layers of greater thickness from acrylic monomer, either the amount of the photoactive s-triazine component (b) should be kept below about 0.5% by weight of the above-identified composition (a) or the intensity of radiation should be reduced so that polymerization proceeds more slowly.

The extent of polymerization can be monitored by measuring the refractive index of the polymerizable mixture. For example, the refractive index may change from about 1.43 for a partially polymerized syrup to about 1.47 at about 100% reaction. The change in refractive index occurs linearly with conversion of the unsaturated moiety. See, for example, discussions about the method in Polymerization at Advanced Degrees of Conversion, G. P. Gladyshev and K. M. Gibov, Keter Press, Jerusalem, 1970.

Alkyl acrylates wherein the alkyl group has 4-12 carbon atoms are readily photopolymerized in the practice of the invention to a pressure-sensitive adhesive state, either alone or in combination with various copolymerizable monoethylenically unsaturated monomers, usually at ratios of about 88-99 parts of the alkyl acrylate or acrylates and correspondingly 12-1 parts by weight of the copolymerizable monomer or monomers.

While the present invention is primarily concerned with pressure-sensitive adhesive tapes, the tack-free products can be used as photo-resists as in the aforementioned U.S. Pat. No. 3,779,778 or as viscoelectric damping material in such applications as in U.S. Pat. No. 3,605,953 (Caldwell et al.) Multifunctional alkyl acrylates such as hexanediol diacrylate and trimethylolpropane triacrylate provide tack-free products. In the absence of alkyl acrylate, alkyl methacrylates also photopolymerize to a tack-free state but without noticeable crosslinking.

In order to enhance the internal strength of polymerized products of the invention, whether or not they are tack-free, the acrylic monomer should include one or more copolymerizable monoethylenically unsaturated monomers which have highly polar groups such as are present in acrylic acid, methacrylic acid, itaconic acid, acrylamide, methacrylamide, N-substituted acrylamides, acrylonitrile, methacrylonitrile, hydroxyalkyl acrylates, cyanoethyl acrylate, N-vinylpyrrolidone, and maleic anhydride. Other useful copolymerizable monoethylenically unsatured monomers include alkyl vinyl ethers, vinylidene chloride, styrene, and vinyltoluene.

Other materials which can be blended with the photoactive mixture of this invention include tackifiers, reinforcing agents, and other modifiers, some of which may copolymerize with the acrylic monomer or photopolymerize independently.

Glass microbubbles having an average diameter of 10 to 200 micrometers can be blended with photoactive mixtures of this invention which polymerize to a pressure-sensitive adhesive state as taught in U.S. Pat. No. 4,223,067 (Levens). If the microbubbles comprise 20 to 65 volume percent of the pressure-sensitive adhesive, the polymerized product will have a foam-like appearance and be suitable for uses to which foam-backed pressure-sensitive adhesive tapes are put.

In the current state of the art, photopolymerization is carried out in an inert atmosphere. Any inert atmosphere such as nitrogen, carbon dioxide, helium or argon is suitable and, as noted above, some oxygen can be tolerated. A sufficiently inert atmosphere can be achieved by covering a layer of the photoactive mixture with a plastic film which is transparent to ultraviolet radiation and irradiating through that film in air.

The peak wavelength of the ultraviolet radiation preferably is close to the wavelength of maximum absorption of the photoactive s-triazine component (b). Good results have been attained using a bank of 40-watt fluorescent black lamps. General Electric and Sylvania each market such a lamp designated "F40BL-Black Light". The GE lamp emits mainly between 310 nm and 430 nm with a maximum at 380 nm. The Sylvania lamp emits mainly between 310 nm and 400 nm with a maximum at 365 nm. Good results have also been obtained with mercury lamps, namely 400 watt and 1000 watt medium-pressure street lights (General Electric HID H400A-33-1). While the fluorescent lamps have been mounted within the chamber which provides an inert atmosphere, the mercury lamps are hotter and were mounted outside the chamber. A sheet of 0.6-cm heat-resistant glass placed 1.3 cm above the coating to be polymerized served to seal the chamber and to filter out radiation below 310 nm.

In using the fluorescent lamps, the operating intensity has usually been adjusted to 2-4 milliwatts/cm² at a distance of 12.5 cm from the coating. The mercury street lights provided an intensity of about 2 milliwatts/cm². The intensity of the irradiation was measured with a United Detector Technology 80X Opto-Meter radiometer which had a sandblasted fused silica diffuser, a Kodak 18A filter, and a silicon photodiode. The filter transmitted light between 300 and 400 nanometers. The radiometer was calibrated in accordance with the spectral output of each lamp.

Pressure-sensitive adhesive tapes of the examples below employed as the backing member biaxially-oriented polyethylene terephthalate film having a thickness of about 2 mils (50 micrometers). Each tape was slit to a width of 1/2 inch (1.27 cm) and had an adhesive thickness of about 2 mils (50 micrometers). Tapes of Examples 1-18 were tested for Peel Value and Shear Value as indicated below. All failures in the tests for Shear Value were cohesive.

PEEL VALUE

Tape is adhered by its adhesive to a glass plate under the weight of a 4.5-kg hard rubber roller. Peelback at 180° is measured by attaching the free end of the tape to a scale and moving the glass plate away from the scale at a rate of about 3.8 centimeters per second.

SHEAR VALUE

A strip of tape is adhered by its adhesive to a stainless steel plate under the weight of a 4.5-kg hard rubber roller with a free end of the tape extending beyond the plate and the adhesive contact area being 1/2 inch by 1/2 inch (1.27 cm by 1.27 cm). After 30 minutes, the plate is placed in an oven at 70° C. and positioned 2° from the vertical to prevent peeling. After 10 minutes in the oven, a one kg mass is suspended from the free end, and the time at which the mass falls is noted. The test is discontinued if the tape has not failed after 10,000 minutes.

EXAMPLES 1 TO 11 AND COMPARATIVE EXAMPLES 1-C TO 7-C

A series of pressure-sensitive adhesive tapes were made by partially photopolymerizing a mixture of, by weight,

90 parts of isooctyl acrylate

10 parts of acrylic acid

0.1 part of 2,2-dimethoxy-2-phenyl acetophenone,

which has the structure ##STR6## and which was obtained as "Irgacure" 651. The partial photopolymerizing was accomplished in an inert (nitrogen) atmosphere using a bank of 40-watt fluorescent black lights (GE as described above) to provide coatable syrups of a viscosity (Brookfield) of about 1500 cps. A photoactive s-triazine was added to each syrup, sometimes together with additional "Irgacure" 651, and thoroughly mixed. Each mixture was coated using a conventional knife coater onto biaxially-oriented polyethylene terephthalate film. The coated film was passed through an inert (nitrogen) chamber and irradiated with the same fluorescent lamps to provide pressure-sensitive adhesive layers. The examples employed the photoactive s-triazines of Table I:

                                      TABLE I                                      __________________________________________________________________________                               Maximum                                                                        absorption                                                                     wavelength                                                                            Extinction                                    Photoactive               in CH.sub.2 Cl.sub.2                                                                  coefficient                                   s-triazine           M.P. °C.                                                                     (nanometers)                                                                          ε × 10.sup.-3                   __________________________________________________________________________     MOST                 190-192                                                                             377    28                                             ##STR7##            145-147                                                                             330    22                                             ##STR8##            150-151                                                                             353    16.5                                           ##STR9##            158-160                                                                             345    5.2                                            ##STR10##           120-123                                                                             350    3.2                                            ##STR11##           90-91                                                                               345    3.9                                            ##STR12##           134-135                                                                             356    17.8                                          __________________________________________________________________________

Structures of the photoactive s-triazines in Table I were confirmed by infrared, nuclear magnetic resonance, and mass spectroscopy. Conditions of the chamber atmosphere, the amount of any additional "Irgacure" 651, the exposure, and the Shear Values in minutes are reported in Table II. All of the tapes had Peel Values of 50-60 ounces per 1/2 inch (110-130 N/100 mm).

                  TABLE II                                                         ______________________________________                                         Ex-                Oxygen                                                      am-  Photoactive   In       Added  Expo- Shear                                 ple  s-triazine    Chamber  Irgacure                                                                              sure  Value                                 No.  Identity Wgt. %   (ppm)  Wgt. % (mj)  (min)                               ______________________________________                                         1-C  MOST     0.10     100    0.15   360      90                               2-C  MOST     0.10      20    0      450   10,000                              3-C  MOST     0.20      20    0.25   450   10,000                              4-C  MOST     0.10      20    0.25   450    1,100                              5-C  MOST     0.10     300    0      450     225                               6-C  MOST     0.10     300    0.25   450    2,800                              7-C  MOST     0.20     300    0      450   10,000                              1    A        0.05     300    0      450   10,000                              2    A        0.10     100    0      150     900                               3    A        0.15     100    0      150   10,000                              4    A        0.10     100    0      225   10,000                              5    B        0.10     100    0      166   10,000                              6    B        0.15     100    0      150   10,000                              7    B        0.2      100    0      125   10,000                              8    C        0.2       30    0      140   10,000                              9    D        0.2       30    0.1    200   10,000                              10   E        0.2       30    0.1    300   10,000                              11   F        0.2       30    0.1    200   10,000                              ______________________________________                                    

EXAMPLES 12 TO 14

A series of pressure-sensitive adhesive tapes were prepared and irradiated as in Examples 1 to 11 except using different acrylic monomers and various photoactive s-triazines as indicated in Table III, except that each photopolymerizable mixture of Examples 12 to 14 employed 0.15 part of Photoactive s-triazine B, Comparative Examples 12-C to 14-C included no photoactive s-triazine, and Example 14 and Comparative Example 14-C included 0.2 part of 2,2-dimethoxy-2-phenylacetophenone.

                  TABLE III                                                        ______________________________________                                                                            Shear                                       Example Acrylic        Photoactive Value                                       No.     Monomers       s-triazine  (min)                                       ______________________________________                                         12      isooctylacrylate:                                                              acrylic acid:                                                                  2-cyanoethyl acrylate                                                          (74:10:16)     B           10,000                                      12-C    isooctylacrylate:                                                              acrylic acid:                                                                  2-cyanoethyl acrylate                                                          (74:10:16)     None        30                                          13      isooctylacrylate:                                                              acrylic acid                                                                   (94:6)         B           10,000*                                     13-C    isooctylacrylate:                                                              acrylic acid                                                                   (94:6)         None        8*                                          14      isooctylacrylate:                                                              N(n-butyl)acrylamide                                                           (66:34)        B           2,400**                                     14-C    isooctylacrylate:                                                              N(n-butyl)acrylamide                                                           (66:34)        None        42**                                        ______________________________________                                          *adhesive contact area 1/2 by 1 inch (1.27 by 2.54                             **adhesive contact area 1/2 by 1 inch (1.27 by 2.54 cm) and tested at roo      temperature                                                              

EXAMPLE 15 AND COMPARATIVE EXAMPLE 15-C

A pressure-sensitive adhesive tape was prepared from a 50% solution in heptane/toluene/methanol 56/24/20 of a 95:5 polymer of 2-ethylhexyl acrylate:acrylamide which had been solution-polymerized to substantially 100% conversion. Photoactive s-triazine B was added to the solution (0.165% of dry weight adhesive) and thoroughly mixed. This was knife-coated [4-mil (0.1 mm) orifice] onto a backing member, dried at 135° C. for 5 minutes, and then irradiated in air using a standard medium-pressure mercury lamp (300 watts/inch) at 30 m/min. (350 mj/cm²). The irradiated tape (Example 15) and an otherwise identical unirradiated tape (Comparative Example 15-C) had Shear Values [except measured at room temperature and a contact area of 1/2 by 1 inch (1.27 cm by 2.54 cm)] of 10,000 and 100 minutes, respectively.

EXAMPLE 16 AND COMPARATIVE EXAMPLE 16-C

A pressure-sensitive adhesive tape was prepared as in Example 15, except that a 94:6 polymer of 2-ethylhexyl acrylate:acrylamide was used and Photoactive s-triazine A was used instead of Photoactive s-triazine B and in an amount of 0.2% of dry weight adhesive, and the solvent was removed by vacuum and heat at a temperature less than 160° C. The dried adhesive was hot-melt coated to a thickness of 2 mils (0.05 mm) and then irradiated in air using the same lamp as in Example 15 at half the web speed (700 mj/cm²). The irradiated tape (Example 16) and an unirradiated tape (Comparative Example 16-C) had Shear Values (measured as in Example 15) of 10,000 and 400 minutes, respectively.

EXAMPLE 17 AND COMPARATIVE EXAMPLE 17-C

A polymer of isooctyl acrylate and acrylic acid (95.5:4.5) was prepared by a conventional emulsion-polymerization technique. The polymer was dried and redissolved in 70:30 heptane:isopropanol, 25% solids. To 100 parts of the solution was added 0.05 part of Photoactive s-triazine B, and this was thoroughly mixed. The mixture was knife-coated [10-mil (0.25 mm) orifice] onto a backing member and dried at 70° C. for 5 minutes. The resulting pressure-sensitive adhesive layer was exposed in the presence of air to ultraviolet irradiation as described in Examples 1-11. The irradiated tape (Example 17) and an otherwise identical unirradiated tape (Comparative Example 17-C) were tested for Peel Value and Shear Value [except 1/2 by 1 inch (1.25 by 2.54 cm) contact area] with results indicated below:

    ______________________________________                                                          Peel Value Shear Value                                        Tape of          (N/100 mm) (minutes)                                          ______________________________________                                         Example 17       37         10,000                                             Comparative Example 17-C                                                                        37            2                                               ______________________________________                                    

EXAMPLE 18 AND COMPARATIVE EXAMPLE 18-C

Tapes were prepared from a commercial pressure-sensitive adhesive which is understood to be a copolymer comprising a major proportion of 2-ethylhexyl acrylate and minor proportions of vinyl acetate, ethyl acrylate and acrylic acid (Ashland "Aroset" 1044-Z-40). This was obtained as a 40% solution, diluted with toluene to 20% solids, and Photoactive s-triazine B (0.15% of dry weight adhesive) was added. After thorough mixing, the solution was knife-coated (0.4-mm orifice) onto a backing member and dried at 70° C. for 15 minutes. The resultant tape (Example 18) was irradiated as in Examples 1-11) in comparison to an unirradiated tape (Example 18-C) which was identical except that it did not have any photoactiive component. Test results were

    ______________________________________                                                            Shear Value                                                 Tape of            (minutes)                                                   ______________________________________                                         Example 18         4380                                                        Comparative Example 18-C                                                                           365                                                        ______________________________________                                    

In each of the pressure-sensitive adhesive tapes of Examples 1 to 18, the adhesive layer was permanently bonded to the polyethylene terephthalate backing member. For many potential uses of the invention, the adhesive layer would be formed on a backing member having a low-adhesion layer from which the adhesive layer could be transferred.

EXAMPLES 19 TO 22 AND COMPARATIVE EXAMPLES 19-C TO 22-C

To investigate further the crosslinking ability of the photoactive s-triazines, polymers were prepared by mixing "Irgacure" 651 (identified in Examples 1-11) or a photoactive s-triazine with various acrylic monomers. Each mixture was purged with nitrogen and irradiated with a bank of 40-watt fluorescent black lights (GE as described above) until substantially complete conversion of the unsaturated moiety. Solubility of the resulting polymers was tested in ethyl acetate after shaking at room temperature for 24 hours, except that Example 20 and Comparative Example 20-C were tested in ethyl acetate/methanol (90/10). Results are shown in Table IV.

                  TABLE IV                                                         ______________________________________                                         Ex-            Photoactive                                                     am-            s-triazine            Sol-                                      ple  Acrylic       (Iden-         Irgacure                                                                              ubil-                                 No.  monomers      tity)   (Wgt %)                                                                               (Wgt %)                                                                               ity                                   ______________________________________                                         19   isooctyl acrylate                                                                            B       0.15   0      gel                                   19-C                       0      0.2    soluble                               20   isooctyl acrylate:                                                                           F       0.15   0      gel                                   20-C acrylic acid          0      0.2    soluble                                    (70:30)                                                                   21   isooctyl acrylate:                                                                           B       0.15   0      gel                                   21-C n-octyl methacrylate  0      0.2    soluble                                    (80:20)                                                                   22   n-butyl acrylate                                                                             B       0.15   0      gel                                   22-C                       0      0.2    soluble                               ______________________________________                                     

I claim:
 1. A photoactive mixture comprising by weight(a) 100 parts of a composition or a polymer of 50-100 parts of acrylic monomer and 0-50 parts of copolymerizable monoethylenically unsaturated monomer and (b) 0.01 to 2 parts of a chromophore-substituted halomethyl-s-triazine of the formula ##STR13## wherein R₁, R₂, R₃, and R₄ are independently hydrogen or alkoxy groups, and 1 to 3 of R₁, R₂, R₃, and R₄ are hydrogen.
 2. A photoactive mixture as defined in claim 1 wherein said alkoxy groups have at most 12 carbon atoms.
 3. A photoactive mixture as defined in claim 2 wherein at least two of said groups are alkoxy.
 4. A photoactive mixture as defined in claim 3 wherein two adjacent alkoxy groups are interconnected to form a ring.
 5. A photoactive mixture as defined in claims 1 or 2 wherein said composition or polymer (a) is a composition which is partially polymerized and has a coatable viscosity of 300 to 20,000 centipoises at ordinary room temperature.
 6. The product of photopolymerizing the partially photopolymerized composition as defined in claim 5 to about 100% conversion of the unsaturated moiety.
 7. A photoactive mixture as defined in claims 1 or 2 wherein said composition or polymer (a) is a polymer of an alkyl acrylate.
 8. A solution of a photoactive mixture as defined in claim 7 in organic solvent.
 9. A photoactive mixture as defined in claim 1 wherein the s-triazine (b) is selected from the group consisting of ##STR14## wherein n is 1, 2 or
 3. 10. A photoactive mixture as defined in claim 1 wherein the composition or polymer (a) comprises a composition or partially polymerized composition of (1) 88-99 parts of alkyl acrylate having 4-12 carbon atoms in its alkyl groups or alkyl acrylates having an average of 4-12 carbon atoms in their alkyl groups and (2) correspondingly 12-1 parts of said copolymerizable monomer and is polymerizable to a pressure-sensitive adhesive state.
 11. A photoactive mixture as defined in claims 1 or 10 wherein at least part of said copolymerizable monomer has highly polar groups.
 12. A photoactive mixture as defined in claim 11 wherein the copolymerizable monomer having highly polar groups is at least one of acrylic acid, methacrylic acid, itaconic acid, acrylamide, methacrylamide, acrylonitrile, methacrylonitrile, N-substituted acrylamides, hydroxyalkyl acrylates, cyanoethyl acrylate, N-vinylpyrrolidone, and maleic anhydride. 